DIFFERENCES BETWEEN POLYAMIDE 6.6 AND POLYAMIDE 6

POLYAMIDE 6,6

FEATURES

POLYAMIDE 6

263 DEGREES

FUSION TEMPERATURE

215 DEGREES

NORMAL

DYE Affinity (Dyeability)

SUPER

LONG TIME MORE DURABLE

EXPOSURE TO SOLAR RADIATIONS

NORMAL

BETTER AT THE MELTING POINT

HIGH TEMPERATURE RESISTANCE

BETTER THAN PA 6.6 IF IT DOESN'T REACH THE MELTING POINT

99 - 100 %

ELASTICITY GAIN AT 5% STRESS

99 - 100 %

4 - 6 LOSS %5

HUMID DURABILITY GRS / DTEX

4 - 6 LOSS %10

30 - 40

35 - 45

ELONGATION % IN HUMIDITY

30 - 40

40 - 50

4,5

OFFICIAL HUMIDITY VALUE

4,5

8 - 10 %

SHRINKING FASTNESS IN BOILING WATER

7 - 9 %

48 °C

60 °C

RECOMMENDED WASHING GRADE ON COLORS

IN WHITE

48 °C

60 °C

150 °C

RECOMMENDED IRON TEMPERATURE

150 °C

210 °C

RECOMMENDED PLEAT TEMPERATURE

180 °C

95 °C

TENSILE TEMPERATURE

95 °C

225 °C

MAXIMUM TEMPERATURE SETTING

190 °C

195 °C

INITIAL LAMINATED TEMPERATURE

160 °C

235 °C

WETTING (WATER ABSORPTION) TEMPERATURE

170 °C

57 °C

VITREOUS TRANSITION TEMPERATURE

50 °C

120 °C

150 °C

205 - 225 °C

THERMOFIX WATER TEMPERATURE SATURATED STEAM

DRYING TEMPERATURE

105 °C

130 °C

180 - 190 °C